Sohail, M G; Salih, M; Al Nuaimi, N and Kahraman, R (2019) Corrosion performance of mild steel and epoxy coated rebar in concrete under simulated harsh environment. International Journal of Building Pathology and Adaptation, 37(5), pp. 657-678. ISSN 23984708
Abstract
Purpose: The purpose of this paper is to present the results of a two-year long study carried out in order to evaluate the corrosion performance of mild steel bare bars (BB) and epoxy-coated rebar (ECR) in concrete under a simulated harsh environment of chlorides. Design/methodology/approach: The blocks are subjected to Southern Exposure testing. The electrochemical impedance spectroscopy (EIS), linear polarization resistance (LPR) and Tafel plot are performed to measure the polarization resistance and corrosion current densities of these rebars. Knife-peel test was performed to assess the adhesion between epoxy and underlying steel after two years of exposure. Findings: Mild steel BB showed a high corrosion current density of 1.24 µA/ cm2 in Tafel plots and a very low polarization resistance of 4.5 kΩ cm2 in LPR technique, whereas very high charge transfer resistance of 1672 and 1675 kΩ cm2 is observed on ECR and ECR with controlled damage (ECRCD), through EIS technique, respectively. EIS is observed to be a suitable tool to detect the defects in epoxy coatings. After two years of immersion in 3.89 percent NaCl− solution, the mild steel BB were severely corroded and a considerable weight loss was observed, whereas under heavy chloride attack, ECR showed no deterioration of epoxy coating and neither any corrosion of underlying steel. Results of this study show that the durability of reinforced concrete (RC) structures with respect to corrosion could be enhanced by using ECR, especially in harsh climatic conditions. Originality/value: The corrosion performance of mild steel and ECR in concrete under a simulating splash zone environment is evaluated. EIS was used to evaluate the health of epoxy and corrosion state of underneath steel rebars. EIS was able to detect the defects in epoxy. The durability of RC structures could be enhanced in harsh climate regions by using ECR.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | accelerated aging conditions; corrosion in reinforced concrete; epoxy-coated rebar; infrastructure durability in harsh climate |
| Index terms: | methodology, corrosion, reinforced concrete, exposure, deterioration, coating, rebar, testing, density, climatic condition, durability, electrochemical impedance spectroscopy |
| Subjects: | engineering analysis, public and environmental health, research methods, building materials, professional practice, analytical methods, material degradation and durability, climate science |
| Topics: | Engineering Principles, Construction Materials, Research Practice, Health and Safety, Sustainability, Urban Studies, Design Practice |
| Descriptive scope: | 4 PCTA |
N.B. Descriptive scope is a count of how many of the five facets of empirical research are indicated by the words used in title, abstract and keywords. It is not intended as a judgement on the research; merely a count of the kind of word we would expect to indicate Phenomenon, Concepts, Theoretical framing, Empirical techniques, Analytical techniques. If all five are present, then a code of “5 PCTEA” will indicate this. If you feel the coding for this record is questionable, we welcome discussion around the terms we matched or the way we categorized them. The facet you would expect may not be coded, or a facet may be coded inappropriately. This can also bear on a larger question, of which facets should be treated as defining in construction management research. Please get in touch, and we will look at it. More details here